控制线和化学注入线
服务
服务
美国德克萨斯州休斯敦的Sandvik服务中心，美国持有广泛的无缝盘绕管和激光焊接的管子，用于控制线和化学注射线，以确保及时交付。它还运行完整的其他服务包：
- 切到长度
- 水久
- Paint striping
- 封装
- Flush and fill (acc. to Nas Class 6)
- Level wound on reels
- Customer specified packaging
- 直接交货到现场
Packing standards
- Coils wound on wooden spools
- 线圈在特定客户的金属卷轴上伤口
- Full package marking service, customer specific
Seamless
Seamless control lines and chemical injection lines
The tables show materials, sizes and approvals for control lines and chemical injection lines in seamless condition.
| 年级 | UNS | C max. | Cr | Ni | Mo | N | 其他 |
|---|---|---|---|---|---|---|---|
| TP 316L | S31600/S31603 | 0.030 | 17.5 | 13 | 2.1 | - | - |
| 合金825 | N08825 | 0.030 | 20 | 38.5 | 2.6 | - | Cu=1.7, Ti=0.7 |
| Sanicro®28 | N08028 | 0.020 | 27 | 31 | 3.5 | - | CU = 1.0 |
| Sandvik SAF 2205™ | S31803/S32205 | 0.030 | 22 | 5 | 3.2 | 0.18 | - |
| Sandvik SAF 2507® | S32750 | 0.030 | 25 | 7 | 4 | 0.3 | - |
* All materials are supplied in the solution annealed condition. Other grades can be offered on request.
| 年级 | Yield strength, psi(MPa) |
Tensile strength, psi(MPa) |
Elongation % |
|---|---|---|---|
| TP 316L | 32,000（220） | 75,000 (515) | 35 |
| 合金825 | 35,000 (240) | 80,000 (550) | 30 |
| Sanicro®28 | 32,000（220） | 100,000（690） | 40 |
| Sandvik SAF 2205™ | 70,000（485） | 99,000（680） | 25 |
| Sandvik SAF 2507® | 80,000 (550) | 116,000 (800) | 25 |
1）溶液退火状况中的所有材料
| 年级 | UNS | pre1） | CPT2）o F （oC) |
Max. H2S3psi | CO24） |
|---|---|---|---|---|---|
| TP 316L | S31600/S31603 | 24 | 95 (35) | 没有限制 | + |
| 合金825 | N08825 | 29 | 140 (60) | 没有限制 | ++ |
| Sanicro®28 | N08028 | 39 | 150 (65) | 没有限制 | ++ |
| Sandvik SAF 2205™ | S31803/S32205 | > 35 | 150 (65) | 1.5 | + |
| Sandvik SAF 2507® | S32750 | >42.5 | 195（90） | 3 | ++ |
1）pre= (%Cr) + 3.3 (%Mo) +16 (%N)
2）Critical Pitting Temperature in neutral solution with approximately 3% chlorides
3）在溶液退火条件下，每NACE MR0175 / ISO 15156用于井下控制线
4）General resistance to CO2corrosion. '++' indicates better resistance than '+'
| 外径 | 室壁厚度 | 最大单线圈长度（TP 316L） | 最大单 coil length (A825) |
Max LLBW1）2） | |||
|---|---|---|---|---|---|---|---|
| 在。 | 在。 | m | ft | m | ft | m | ft |
| 1/4 | 0.035 | 252 | 827 | 640 | 2,100 | 29,000 | 95,149 |
| 1/4 | 0.049 | 192 | 630 | 488 | 1,601 | 22,000 | 72,182 |
| 1/4 | 0.065 | 158 | 518 | 401 | 1,316 | 18,000 | 59,058 |
| 3/8 | 0.035 | 159 | 522 | 404 | 1,326 | 18,000 | 59,058 |
| 3/8 | 0.049 | 118 | 387 | 300 | 984 | 14,000 | 45,934 |
| 3/8 | 0.065 | 94 | 308 | 239 | 784 | 11,000 | 36,091 |
| 3/8 | 0.083 | 78 | 256 | 199 | 653 | 9,000 | 29,529 |
| 1/2 | 0.035 | 116 | 381 | 296 | 971 | 13,000 | 24,653 |
| 1/2 | 0.049 | 85 | 279 | 217 | 712 | 10,000 | 32,810 |
| 1/2 | 0.065 | 67 | 220 | 171 | 561 | 7,500 | 24,608 |
| 1/2 | 0.083 | 55 | 180 | 139 | 456 | 6,000 | 19,686 |
| 5/8 | 0.035 | 92 | 302 | 234 | 767 | 10,750 | 35,271 |
| 5/8 | 0.049 | 67 | 220 | 171 | 561 | 7,500 | 24,608 |
| 5/8 | 0.065 | 52 | 171 | 131 | 430 | 6,100 | 20,014 |
| 5/8 | 0.083 | 25 | 82 | 25 | 82 | 5,000 | 16,405 |
| 3/4 | 0.035 | 25 | 82 | 25 | 82 | - | - |
| 3/4 | 0.049 | 25 | 82 | 25 | 82 | - | - |
| 3/4 | 0.065 | 25 | 82 | 25 | 82 | - | - |
| 3/4 | 0.083 | 25 | 82 | 25 | 82 | - | - |
1）Long length butt welded
2）For 3/4 in. OD single coils can be made. Contact us for complete details.
批准
- ISO 9001:2000
- ISO 14001：2004
- OHSAS 18001
- PED 97/23/EC
- ANSI NACE MR 0175 / ISO 15156
焊接
焊接控制线和化学注射线
这些表显示了在焊接条件下的控制线和化学注射线的材料，尺寸和批准。
| 年级 | UNS | C 最大限度。 |
Cr | Ni | Mo | 其他 |
|---|---|---|---|---|---|---|
| TP 316L | S31600/S31603 | 0.030 | 17.5 | 13 | 2.1 | 0.1 |
| 合金825 | N08825 | 0.030 | 20 | 38.5 | 2.6 | Cu=1.7, Ti=0.7 |
| 合金625 | N6625 | 0.10 | 21.5 | > = 58 | 9 | Nb=3.5 |
*All materials are supplied in the solution annealed condition. Other grades can be offered on request.
| 年级 | Yield strength, psi(MPa) |
Tensile strength, psi(MPa) |
Elongation % |
|---|---|---|---|
| TP 316L | 32,000（220） | 75,000 (515) | 35 |
| 合金825 | 35,000 (240) | 80,000 (550) | 30 |
| 合金625 | 60,000 (415) | 110000 (760) | 30 |
1）溶液退火状况中的所有材料
| 年级 | UNS | pre1） | CPT2）F （oC) | Max H2S3）psi | CO24） |
|---|---|---|---|---|---|
| TP 316L | S31600/S31603 | 24 | 95 (35) | 没有限制 | + |
| 合金825 | N08825 | 29 | 140 (60) | 没有限制 | ++ |
| 合金625 | N06625 | 52 | 195（90） | 没有限制 | ++ |
1）pre= (%Cr) + 3.3 (%Mo) +16 (%N)
2）Critical Pitting Temperature in neutral solution with approximately 3% chlorides
3）在溶液退火条件下，每NACE MR0175 / ISO 15156用于井下控制线
4）General resistance to CO2corrosion. '++' indicates better resistance than '+'
Size range (in.)
该表显示了库存标准尺寸。可以根据要求提供其他尺寸。
| OD | wt | OD | wt | OD | wt | OD | wt | OD | wt |
|---|---|---|---|---|---|---|---|---|---|
| 1/4 | 0.035 | 3/8 | 0.035 | 1/2 | 0.035 | 5/8 | 0.035 | 3/4 | 0.035 |
| 1/4 | 0.049 | 3/8 | 0.049 | 1/2 | 0.049 | 5/8 | 0.049 | 3/4 | 0.049 |
| 1/4 | 0.065 | 3/8 | 0.065 | 1/2 | 0.065 | 5/8 | 0.065 | 3/4 | 0.065 |
| - | - | 3/8 | 0.083 | 1/2 | 0.083 | 5/8 | 0.083 | 3/4 | 0.083 |
OD = Outside diameter, WT = Wall thickness
批准
- ISO 9001:2000
- Intertek
- MGMT. SYS. RvA 050
- ANAB
封装
封装materials
Sandvik提供了广泛的封装材料。最常见的方法可以在下表中找到。可以根据要求提供其他封装材料。
Material rating on a scale of 1 to 5 (1=not good, 5=excellent)
| Materials | 最大温度。 of（co) |
Abrasion resistance | 抵抗inhibited brine well fluids | 抵抗 oil/diesel well fluids |
|---|---|---|---|---|
| Polypropylene | 150 (65) | 2 | 5 | 3 |
| 尼龙11 | 200 (93) | 4 | 3 | 3 |
| PVC | 174 (79) | 3 | 2 | 3 |
| TPV | 275 (135) | 3 | 5 | 3 |
| Halar | 300 (149) | 4 | 4 | 5 |
| PVDF | 310 (154) | 4 | 3 | 5 |
| MPH340G | 340 /171） | 4 | 4 | 5 |
压力表
压力表
Selection of the appropriate material for any given control or chemical injection line is subject to the prevailing operational and site conditions. In order to assist in the selection, the following tables provide internal pressure ratings and the adjustments factors for a range of common grades and sizes of seamless and laser welded stainless tubing.
TP 316L在100°F（38°C）下的最大压力（P）1）
Please refer to grade and product form adjustment factors below.
| 外径，IN。 | 壁厚，IN。 | 工作压力2） psi(MPa) |
爆破压力2） psi(MPa) |
塌陷压力4） psi(MPa) |
|---|---|---|---|---|
| 1/4 | 0.035 | 6,600 (46) | 22,470（155） | 6,600 (46) |
| 1/4 | 0.049 | 9,260（64） | 27,400 (189) | 8,710（60） |
| 1/4 | 0.065 | 12,280（85） | 34,640 (239) | 10,750(74) |
| 3/8 | 0.035 | 4,410 (30) | 19,160 (132) | 4,610 (32) |
| 3/8 | 0.049 | 6,170（43） | 21,750（150） | 6,220 (43) |
| 3/8 | 0.065 | 8,190 (56) | 25,260（174） | 7,900（54） |
| 3/8 | 0.083 | 10,450（72） | 30,050（207） | 9,570 (66) |
| 1/2 | 0.049 | 4,630 (32) | 19,460 (134) | 4,820 (33) |
| 1/2 | 0.065 | 6,140 (42) | 21,700 (150) | 6,200（43） |
| 1/2 | 0.083 | 7,840 (54) | 24,600（170） | 7,620 (53) |
| 5/8 | 0.049 | 3,700（26） | 18,230 (126) | 3,930 (27) |
| 5/8 | 0.065 | 4,900 (34) | 19,860 (137) | 5,090 (35) |
| 5/8 | 0.083 | 6,270（43） | 26,910 (151) | 6,310（44） |
| 3/4 | 0.049 | 3,080 (21) | 17,470（120） | 3,320（23） |
| 3/4 | 0.065 | 4,090（28） | 18,740（129） | 4,310 (30) |
| 3/4 | 0.083 | 5,220 (36) | 20,310（140） | 5,380（37） |
1）Estimates only. Actual pressures should be calculated considering all stress factors in the system.
2）Based on calculations from API 5C3, using a wall tolerance of +/-10%
3）基于极限强度突然calculations from API 5C3
4）基于API 5C3的屈服强度崩溃计算
工作压力限制的调整因素1）
PW =在100°F（38°C）下TP 316L的参考工作压力等级。为了确定坡度/温度组合的工作压力，请乘以调节因子乘以PW。
| 年级 | 100°F (38°C) |
200°F (93°C) |
300°F (149°C) |
400°F (204°C) |
|---|---|---|---|---|
| TP 316L, seamless | 1.00 | 0.87 | 0.70 | 0.63 |
| TP 316L，焊接 | 0.85 | 0.74 | 0.60 | 0.54 |
| Sandvik Saf 2205™，无缝 | 2.17 | 2.00 | 1.77 | 1.60 |
| Sandvik SAF 2205™, welded | 1.84 | 1.70 | 1.50 | 1.36 |
| 合金825，无缝 | 1.33 | 1.17 | 1.10 | 1.03 |
| 合金825，焊接 | 1.13 | 0.99 | 0.94 | 0.88 |
| Sandvik SAF 2507®， 无缝的 | 2.67 | 2.33 | 2.17 | 1.70 |
| Sandvik SAF 2507®，焊接 | 2.27 | 1.98 | 1.84 | 1.45 |
1）基于ASME的允许应力的调整因子。
Example: The maximum factors allowable working pressure for seamless 1/2 x 0.049 in. Sandvik SAF 2507®管道at 100°F (38°C) can be calculated as:
4,630 psi – Pressure rating for TP 316L at 100°F (38°C)
x 2.67 – Adjustment factor for Sandvik SAF 2507, seamless at 100°F (38°C)
12,362 PSI - Sandvik SAF 2507的工作压力等级®管道
爆发压力限制的调整因子1）
Pb =在100°F下TP 316L的参考突发压力。为了确定成绩/温度组合的爆发压力，请乘以调节因子乘以PB。
| 年级 | 100°F (38°C) |
200°F (93°C) |
300°F (149°C) |
400°F (204°C) |
|---|---|---|---|---|
| TP 316L, seamless | 1.00 | 0.93 | 0.87 | 0.80 |
| TP 316L，焊接 | 0.85 | 0.79 | 0.74 | 0.68 |
| Sandvik Saf 2205™，无缝 | 1.71 | 1.33 | 1.20 | 1.07 |
| Sandvik SAF 2205™, welded | 1.45 | 1.13 | 1.02 | 0.91 |
| 合金825，无缝 | 1.13 | 1.07 | 1.00 | 0.87 |
| 合金825，焊接 | 0.96 | 0.91 | 0.85 | 0.74 |
| Sandvik SAF 2507®， 无缝的 | 1.97 | 1.75 | 1.57 | 1.35 |
| Sandvik SAF 2507®，焊接 | 1.64 | 1.47 | 1.31 | 1.13 |
1）基于ASME的最终强度的调整因素。
示例：无缝3/8 x 0.049英寸的最大因素爆发压力。SANDVIKSAF 2507®在200°F（93°C）处的管道可以计算为：
21,750 psi – burst pressure rating for TP 316L at 100°F (38°C)
x 1.73 - Sandvik SAF 2507的调整系数，在200°F（93°C）处无缝
37,627 psi – burst pressure rating for Sandvik SAF 2507®管道
调整因素倒塌压力极限1）
PC =在100°F（38°C）下TP 316L的参考塌陷压力额定值。为了确定成绩/温度组合的崩溃压力，请乘以调节因子乘以PC。
| 年级 | 100°F (38°C) |
200°F (93°C) |
300°F (149°C) |
400°F (204°C) |
|---|---|---|---|---|
| TP 316L, seamless | 1.00 | 0.87 | 0.70 | 0.63 |
| TP 316L，焊接 | 0.85 | 0.74 | 0.60 | 0.54 |
| Sandvik Saf 2205™，无缝 | 2.17 | 2.00 | 1.77 | 1.60 |
| Sandvik SAF 2205™, welded | 1.84 | 1.70 | 1.50 | 1.36 |
| 合金825，无缝 | 1.33 | 1.17 | 1.10 | 1.03 |
| 合金825，焊接 | 1.13 | 0.99 | 0.94 | 0.88 |
| Sandvik SAF 2507®， 无缝的 | 2.67 | 2.33 | 2.17 | 1.70 |
| Sandvik SAF 2507®，焊接 | 2.27 | 1.98 | 1.84 | 1.45 |
1）基于ASME的屈服强度的调整因子。
Example: The maximum factors collapse pressure for seamless 1/4 x 0.035 in. Alloy 825 tubing at 200°F (93°C) can be calculated as:
6,600 psi - 在100°F（38°C）下ASTM 316L的塌陷压力等级
x 1.17 – Adjustment factor for Alloy 825 seamless at 200°F (93°C)
7,722 psi – Collapse pressure rating for Alloy 825 tubing